A 100Cr6 (AISI E52100) steel in the hardness range of 180 to 750 HV10 was machined. Quick stop tests were carried out at various hardness values to observe the different chip formation mechanisms. A limit was found between the shearing and cracking chip formation. Experiments on the selected steel a...